Rod-like mesoporous silica nanoparticles with pH-responsive amphiphilic hyperbranched polyester shells were prepared for doxorubicin (DOX) delivery. First, rod-shaped mesoporous silica nanoparticles (MSNs) were obtained, then hydrophobic hyperbranched polyester Boltorn H40 (H40) was grafted on their surface. The H40 coated MSNs were next treated with amine-functionalized polyethylene glycol (PEG) to achieve the hydrophilic and pH-responsive material denoted as PEG-H40-MSNs.
The experimental results showed that PEG-H40-MSNs were successfully synthesized. BET analysis showed that rod MSNs exhibits a type IV standard isotherm. TEM revealed that the thin gray polymer layer was formed around the SBA-15 particle with a diameter of around 150 nm. DOX was effectively loaded, which can be released according to the ambient pH inside the cell as follow: at pH 7.4, only 9.7% of the DOX was released after 48 h; as the pH decreased to 5.5, the cumulative release reached to 49% at the same time.
PEG-H40-MSNs showed less than 1.6% of hemolytic activity and a slight effect on the liver and kidney of treated mice were observed at a high disposal dosage implying negligible toxicities were caused by PEG-H40-MSNs in both in vitro hemolysis analysis and in vivo biochemical in mice. However, the in vitro cytotoxicity evaluation of the DOX-PEG-H40-MSNs showed that the cell cytotoxicity of both pure DOX and DOX-loaded PEG-H40-MSNs generally enhanced by increasing the concentration of DOX. Continue on Amphiphilic hyperbranched polyester coated rod mesoporous silica nanoparticles for pH-responsive doxorubicin delivery